Water Based One Component Acrylic Waterproof Paint

Green environmental protection products / Water-based emulsion / Does not contain any organic solvent / Non-toxic harmless /Can be constructed on the wet base / High bond strength / The film has high strength / High elongation / Strong adaptability to base shrinkage and deformation cracking

Category:

Water Based waterproof coating

Keywords:

Water-based industrial coatings

Online Consultation

Product features

* Water-based emulsion, does not contain any organic solvent, non-toxic harmless, is a green environmental protection products

* Can be constructed on the wet base, high bond strength

* The film has high strength, high elongation, and strong adaptability to base shrinkage and deformation cracking

* Good low temperature bending performance (bending at -10℃ without crack)

* Single component, cold construction, namely out of the box, easy constructio

Packaging / Transportation and Storage

* The product is packed in clean, dry and airtight plastic drums.

* This product is non-flammable and explosive material, can be transported as general goods. During transportation, it should be protected from freezing, rain, exposure, extrusion and collision, and keep the package intact.

* The product in storage should be ventilated, dry, prevent direct sunlight.

* Storage and transportation temperature must be kept at 5℃ ~ 35℃, lower than 5℃ should take heat preservation measures.

* Under normal transportation and storage conditions, the shelf life is 12 months.

Standard Parameters of water based polyurethane waterproof paint(refer to JC/T864-2008)
Items		Indicator
Tensile strength/Mpa≥		1
Fracture elongation /%≥		300
low temperature flexibility		-10℃ no crack
Impermeability		0.3Mpa, 30min
Solid content%≥		65
drying time	Surface dry ≤	4h
	hard dry≤	8h
Tensile strength retention after treatment%	Heat treatment≥	80
	Alkali treatment≥	60
	Acid treatment≥	40
	Artificial weather aging treatment≥	80-150
Fracture elongation after treatment ,%	Heat treatment≥	200
	Alkali treatment≥
	Acid treatment≥
	Artificial weathering treatment≥	200
Heating expansion rate%	Elongation≤	1
	shorten ≤	1