Water Based Two-Component Epoxy Zinc - Rich Primer

1. Water as dispersion medium, no danger of explosion, easy to use<br> 2. Fast drying of paint film can reduce construction cost and improve construction efficiency<br> 3. Strong adhesion, tough film, high impact strength<br> 4. Cathodic protection, excellent rust resistance

Category:

Water Based heavy anti-corrosion series

Keywords:

Water-based industrial coatings

Online Consultation

Product features

* Water as dispersion medium, no danger of explosion, easy to use

* Fast drying of paint film can reduce construction cost and improve construction efficiency

* Strong adhesion, tough film, high impact strength

* Cathodic protection, excellent rust resistance

Application

Used for anticorrosion of iron and steel material, it is the choice primer of long - term waterborne heavy anticorrosion coating. For example: ships, containers, platforms, docks and other Marine facilities, petrochemical pipelines and storage tanks, metallurgy, electric power, food , textile and other industries in the steel components of the long-term rust and corrosion.

Base material treatment

Sand blasting or grinding to Sa2.5 or St3 level, that is, thoroughly remove the rust layer and the old paint film, exposing the metal luster of the bottom material

Packing specification

Component A 22.5kg/ barrel

Component B 7.5kg / barrel

Storage life

Stored in 0 ~ 40℃, cool, clean, dry place

Storage life is six months

Transportation

Avoid sun and rain during transportation, and carry out according to the relevant provisions of non-dangerous goods

Note

1. This product is water-based paint, can not be mixed with organic solvents or solvent based paint.

2. The two components should be thoroughly mixed and mixed with a portable electric mixer.

3. Mix lacquers for application according to requirement , avoiding waste.

4. Soak the new brush in a mixture of washing powder and baking soda for half an hour before use, and then rinse with water.

5. Wash tools with water immediately after use.

6. It is not suitable for construction when the temperature is lower than 0℃ and the relative humidity is higher than 85%

Standard parameters of waterborne epoxy resin anti-corrosion coatings (refer to HG/T 4759-2014)
project		index
		primer	Intermediate paint	topcoat
state in the container		normal
Appearance of paint film		normal
Nonvolatile content%≥		40
drying time	Surface dry, h≤	4
	hard work, h≤	twenty four
Bending test/mm≤		3
Impact resistance/cm≥		40
Cross-cut test/level≤		1
Storage stability [(50±2)℃, 14d		normal
Volatile organic compound (VOC) content/(g/L)≤		200
Flash rust inhibition		normal
Water resistance (240h)		normal
Salt spray resistance (300h)		No blister, no rust, no peeling